NILA®-Plast GP 3.0-W (Type II)

Name: NILA®-Plast GP 3.0-W (Type II)
Brand: NILA
SKU: nila-plast-gp-3-0-w

Hot plastic compound suitable for laying both on and in areas for type II markings, traffic class P7

Want to order or have questions?

Get in touch – we'll help you choose the right products, advise on usage and prepare a quote.

+370 6 858 5782 andrius@biguma.lt

Description

NILA®- Plast GP 3.0-W (Type II) is a high-quality thermoplastic marking material for making markings on all types of traffic surfaces made of asphalt, such as roads, motorways, sports surfaces, airfields and car parks. Enhanced night visibility (retroreflection) in wet conditions is achieved by the large glass beads mixed into the compound and the extra addition of high-quality glass beads. The thermoplastic is distinguished by a high softening point, excellent deformation resistance, low abrasion and good grip with very good adhesion and laying properties. NILA®- Plast GP 3.0-W (Type II) is available in 25 kg flat cartons, 20 kg polyethylene bags and 250 kg big bags.

Technical standards: DIN EN 1436, ZTV M 13

Advantages

Hot plastic compound for type II markings
Hot plastic compound suitable for laying both on and in areas
Premium marking material with stone dust, sand and glass beads
High softening point, resistance to deformation, low abrasion
Good grip with excellent adhesion and easy to use

Available packaging

Flat carton (block goods): 25 kg (40 per pallet). Polyethylene bag (powder goods): 20 kg (42 per pallet). Big bag (powder goods): 250 kg (4 per pallet).

Downloads

Technical datasheet

Download PDF file

Technical info

Application instructions

Application

NILA®-Plast GP 3.0-W is applicable at temperatures from 180 to 210 °C in a layer thickness of 3 mm, screwed or extruded or screwed and inlaid in layer thickness 3/5 mm or 6/8 mm. During application 500 g/m² drop-on material WEISSKER DUOLUX® 121 AH 1 (125–1180 µm) 3:1 must be dropped on to the thermoplastic immediately to reach the required night-time visibility. The night-time visibility in wet conditions will be achieved by the rough surface of the onlaid or inlaid thermoplastic and the embedded drop-on beads and further on by the greater diameter premix glass beads. The road surface must be dry, clean and free of dust and oil. In spring and autumn the relative humidity of the air (dew point) must be considered. If the minimum air temperature is below +5 °C, the road surface must be warmed before application. More consumption in case of roughness of the underground must be separately calculated.

Material consumption

At 3 mm layer thickness: 6.18 kg/m². Width-based: 10 cm → 618 kg/1,000 m; 12 cm → 742 kg/1,000 m; 15 cm → 927 kg/1,000 m.

Storage

Shelf life of block material is unlimited. Shelf life of powder material is one year.

Technical data

Base	Hydrocarbon resin, quartz sand, extender
Solvent	Solvent-free
Colour	White
Necessary working operations	1
Specific gravity	approx. 2.06 g/cm³
Softening point Wilhelmi	approx. 101 °C
Nüssel deformation	approx. 1.0
Skid resistance	≥ 45 SRT-units
Dry weight	100%
Wear resistance (BASt, 4M roll-overs)	≥ 90% (class P7, ZTV M 13)